Chalco Aluminum Coat lacquered 3102 8011 aluminum coil strip fin stock for heat exchanger have two types, one is normal hydrophilic 3102 8011 aluminum coil strip (blue),and the other is high corrosion of hydrophilic aluminium foil( Golden)....
Chalco Aluminum Coat lacquered 3102 8011 aluminum coil strip fin stock for heat exchanger have two types, one is normal hydrophilic 3102 8011 aluminum coil strip (blue),and the other is high corrosion of hydrophilic aluminium foil( Golden).
Normal hydrophilic aluminum foil coated in blue color, this lacquered 3102 8011 aluminum coil strip makes the condensated water drop to become a layer avoiding the feasibility of ice bridges. It allows to produce smaller equipment.
High corrosion of hydrophilic 3102 8011 aluminum coil strip coated in golden color, is an excellent solution of coating against corrosion of the fin. Expoxy resins based on highly specific to this application, provides the desired protection in a wide range of colours.
Specs of 3102 8011 aluminum coil strip fin stock:
Alloy: 8011, 3102
Temper: O, H22, H24, H26
Thickness: 0.10mm--0.20mm
Width: 100mm---500mm
|
Alloy |
Temper |
Thickness/mm |
Tension strength/MPa |
Elongation A50 % |
Cupping value
|
|
8011 |
H22 |
0.10mm--0.20mm |
110--120 |
16--25 |
6.0--7.0 |
|
H24 |
115--135 |
12--17 |
5.0--6.0 |
||
|
H26 |
140--160 |
8--12 |
4.0--5.0 |
||
|
3102 |
H26 |
125--145 |
14--16 |
5.5--6.5 |
|
|
Normal hydrophilic aluminum coil strip |
High corrosion of hydrophilic aluminium coil strip |
|
Advantages |
1. Very good finishing, high thermal conductivity, good drawability and low density. 2. Collars height up to 12mm could be obtained(depending of the thickness and haracteristics of metal). 3. Studies performed by specialized in independent organisms demonstrate that does not favor the growth of micro-organisms. 4. With high hydrophilic preperties its is the best choosing for standard environments. 5. It is also possible to incorporate our pre-treatment systems that improve the protection against corrosion and the lacquer adherence over the aluminium surface. |
1. The polymers with high degree of reticulation aluminium lining prevent aggressive agents come in touch with the metal, they themselves being ver resistant to corrosion, the fins are at least 300% more resistant to corrosion than bare aluminum. 2. Very good finishing, high thermal conductivity, good drawability and low density. 3. Collars height up to 12mm could be obtained. 4. Finishing have been developed to have highest possible resistance to scratches. 5. Studies performed by specialized independent organisms demonstrate that this foil does not favour the growth of micro organisms. 6. It is also possible to incorporate our pre-treatment systems that improve the protection against corrosion and the lacquer adherence over the aluminium surface. |
|
Applications |
Chalco Aluminum coat supplies its product normal hydrophilic aluminum foil, can be used for the development of the following applications:
Heat exchangers for food industry. Heating and air conditioning systems for buildings. Heat exchangers for car, ship and airplanes. |
Chalco Aluminum coat supplies high corrosion of hydrophilic aluminium foil, can be used for high corrosion resistance of the following applications:
Heat exchangers for food industry. Heating and air conditioning systems for buildings. Heat exchangers for car, ship and airplanes. |
|
Product description |
Aluminium foil from 100 to 300 um with silica based or silica free lacquer for both sides. |
Aluminium foil from 100 to 300 um with epoxy based lacquer, PU based lacquer, or EPPU double layer for both sides. |
Recommended alloys:
8011, 1100, 3102 alloy, customer can specify its needs in order to choose the best thickness, alloy and temper of the metal.
Coating properties compare:
|
Property |
Test |
Normal hydrophilic aluminum foil |
High corrosion of hydrophilic aluminium foil |
|
Nature |
|
Hydrophilic |
PET |
|
Colors |
|
Blue |
Gold |
|
Wettability |
UNE EN546-4 |
A-B |
E |
|
Adherence |
ASTM D-3359 |
OK |
OK |
|
Bending |
ECCA 7(0≤ T BEND ≤1) |
OK |
OK |
|
Drawing |
ECCA T6-ISO 1520 (5mm) |
OK |
OK |
|
Curing |
Resistance to MEK |
> 10 d.f. |
>50 d.f. |
|
Heat Resistance |
200℃/5 min. |
OK |
OK |
|
Solvent Resistance |
TRICHLOROETHYLENE(85℃/5 min.) |
Weight loss<1% |
Weight loss<1% |
|
PERCHILOROETHYLENE(120℃/5 min.) |
Weight loss<1% |
Weight loss<1% |
|
|
Corrosion Resistance(Neutral Salt Spray) |
ASTM B117 (NaCI 5%/35℃ |
Up to 300 h |
Up to 1000h(According to specs) |
|
Contact angle(distilled water) |
Initial |
<10° |
|
|
Kesternich Test Resistance |
ISO 3231 (0.21 SO2) |
|
Up to 15 cycles( According to specs) |
|
Humidity Test |
DIN 50017 /1000h) |
|
No modification, no corrosion |
|
U.V. Resistance |
ASTM G154 (500h: UV-313 4h. 60 ℃/Condensation 4h 40℃ |
|
OK |